Vanadium

Vanadium, ₂₃V

Vanadium pāndaniyum·
Pabaosan	/vəˈneɪdiəm/ ​(və-NAY-dee-əm)
Cingakan	logam pelung-pérak-klau
Bobot atom standar Ar, std(V)	7001509415000000000♠50.9415(1)[1]
Vanadium ring tabél périodik
Hidrogén Hélium Litium Bérilium Boron Karbon Nitrogén Oksigén Fluorin Néon Natrium Magnésium Aluminium Silikon Phosfor Urirang Klorin Argon Potasium Kalsium Skandium Titanium Vanadium Kromium Mangan (datu) Wesi Kobalt Nikel Temaga Séng Gallium Gérmanium Arsenik Sélénium Brom Kripton Rubidium Strontium Ittrium Zirkonium Niobium Molibdénum Téknésium Ruthénium Rhodium Palladium Pérak Kadmium Indium Timah Antimoni Téllurium Yodium Xénon Sésium Barium Lanthanum Sérium Praséodimium Néodimium Prométhium Samarium Éuropium Gadolinium Terbium Disprosium Holmium Érbium Thulium Itterbium Lutésium Hafnium Tantalum Tungstén Rhénium Osmium Iridium Platinum Mas Rasa (datu) Thallium Timbal Bismuth Polonium Astatin Radon Fransium Radium Aktinium Thorium Protaktinium Uranium Néptunium Plutonium Amérisium Curium Berkélium Kalifornium Éinsteinium Fermium Méndelevium Nobélium Lawrénsium Rutherfordium Dubnium Seaborgium Bohrium Hassium Meitnérium Darmstadtium Roéntgénium Kopernikium Nihonium Flérovium Moskovium Livermorium Ténnessin Oganésson – ↑ V ↓ Nb titanium ← vanadium → kromium
Wilangan atom (Z)	23
Watek	golongan 5
Période	période 4
Blok	blok-d
Konpigurasi éléktron	[Ar] 3d3 4s2
Éléktron per kulit	2, 8, 11, 2
Cecirén pisik
Pase ring STP	padet
Titik lebur	2183 K ​(1910 °C, ​3470 °F)
Titik didih	3680 K ​(3407 °C, ​6165 °F)
Kapadetan (nampek s.r.)	6.11 g/cm3
ri kala éncéh (ring t.l.)	5.5 g/cm3
Panes fusi	21.5 kJ/mol
Panes panguapan	444 kJ/mol
Kapasitas panes molar	24.89 J/(mol·K)
Tekanan uap P (Pa) 1 10 100 1 k 10 k 100 k at T (K) 2101 2289 2523 2814 3187 3679
Cecirén atom
Paindikan oksidasi	−3, −1, 0, +1, +2, +3, +4, +5 (oksida ampotér)
Kaéléktronégatipan	skala Pauling: 1.63
Wasa ionisasi	ka-1: 650.9 kJ/mol ka-2: 1414 kJ/mol ka-3: 2830 kJ/mol (malih)
Jeriji atom	émpiris: 134 pm
Jeriji kovalén	153±8 pm
Garis spéktral saking vanadium
Cecirén liyanan
Rupa alami	primordial
Struktur kristal	​kubus mapusat badan (bcc)
Kagelisan swara pales tipis	4560 m/s (ring 20 °C)
Ékspansi térmal	8.4 µm/(m⋅K) (ring 25 °C)
Konduktivitas térmal	30.7 W/(m⋅K)
Resistivitas listrik	197 nΩ⋅m (ring 20 °C)
bacakan magnétik	paramagnétik
Karentanan magnétik molar	6996254999999999999♠+255.0×10−6 cm3/mol (298 K)[2]
Modulus Young	128 GPa
Modulus Shear	47 GPa
Modulus Bulk	160 GPa
Rasio Poisson	0.37
Kakatosan Mohs	6.7
Kakatosan Vickers	628–640 MPa
Kakatosan Brinell	600–742 MPa
Nomor CAS	7440-62-2
Lelintihan
Panemuan	Nils Gabriel Sefström (1830)
Isolasi kapertama	Henry Enfield Roscoe (1867)
Kaaranin olih	Nils Gabriel Sefström (1830)
Isotop utama vanadium
Iso­top Kalimpahan Paruh-idup (t1/2) Mode paluruhan Pro­duk 48V syn 16 d β+ 48Ti 49V syn 330 d ε 49Ti 50V 0.25% 1.5×1017 y ε 50Ti β− 50Cr 51V 99.75% tegteg
Kategori:Vanadium cingak pabligbagan uah | pustaka

Vanadium silih tunggil datu kimia antuk simbol V miwah wilangan atom 23. Punika logam transisi katos, klau masawang pérak, kalis. Datu logam kapah katemuin ring palemahan, menawi sesampun kaisolasi sacara karyanan, pawentukan lapisan oksida (pasivasi) akedik negtegang logam bébas majeng oksidasi luwih lantur.